Recycled Glass-Filled Polyamide PA6
Description
Material Wizard produces property-restored recycled glass-filled polyamides. The polyamide regranulate can be used as a replacement for the original material or blended with it.
Key properties
- Strength
- Stiffness
- Acceptable electrical insulation properties
- Increased resistance to thermal loads
Applications
Load-bearing household products, transformer bobbins, gears, socket and switch components.
Parameter
Unit
Value
Physical properties:
Density
g/cm³
1,36 (ISO 1183-1)
Glass fiber content
%
30 (ISO 3451-1)
Moisture absorption, maximum
%
9 (ISO 62)
Moisture content at saturation
%
5 (ISO 1110)
Rheological properties:
Melt flow rate (MFR) 275 °C, 2.16 kg
g/10 min
10 (ISO 1133-1)
Melt flow rate (MFR) 290 °C, 2.16 kg
g/10 min
15 (ISO 1133-1)
Mold shrinkage, longitudinal
%
0,1 (ISO 294-4)
Mold shrinkage, transverse
%
0,5 (ISO 294-4)
Mechanical properties:
Flexural strength
MPa
160 (ISO 178)
Charpy impact strength, +23 °C
kJ/m²
40 (ISO 179-1/1eA)
Charpy notched impact strength, +23 °C
kJ/m²
5 (ISO 179-1/1eA)
Tensile elongation
%
4 (ISO 527-1/-2)
Thermal properties:
Melting temperature
°C
210 (ISO 11357-3)
Recommended maximum temperature for short-term thermal loads
°C
150
Flammability
class
HB (UL 94)
Oxygen index
%
26 (ISO 4589-2)
*
Typical data for this polymer class, for reference.
The stated values are measured by internal test methods close to the corresponding ISO and GOST standards.
The information is for reference only; we recommend using the technical data after agreement with the supplier and signing of a normative technical specification.