Glass-filled polyamide Examid PA6 GF10
Description
Examid® PA6 GF10 is a 10 % glass fiber reinforced polyamide 6 for injection molding. Its key characteristics include good tensile and flexural strength, moderate rigidity, excellent heat resistance and easy processing.
Advantages
- High mechanical strength
- Excellent impact resistance
- Reduced moisture absorption
Applications
The material is intended for use in electrical and electronic devices, automotive components, industrial equipment, household appliances and consumer goods requiring reliable mechanical and thermal performance.
The listed values are measured by internal methods close to the corresponding ISO and GOST standards. This information is for reference only and is not an official batch data sheet. Please request the TDS and MSDS for a specific batch before industrial use.
Parameter
Unit
Value
Physical properties:
Density
g/cm³
1.23 (ISO 1183-1)
Glass fiber content
%
10 (ISO 3451-1)
Melt flow rate (MFR, 235 °C / 2.16 kg)
g/10 min
12 (ISO 1133-1)
Mechanical properties:
Tensile strength
MPa
110 (ISO 527-1/-2)
Charpy impact strength (notched, 23 °C)
kJ/m²
11 (ISO 179-1/1eA)
Flexural strength
MPa
180 (ISO 178)
Elongation at break
%
8 (ISO 527-1/-2)
Tensile modulus
MPa
5000 (ISO 527-1/-2)
UL 94 flammability rating (3.0 mm)
—
HB* (IEC 60695-11-10)
Tensile modulus (2)
MPa
5000* (ISO 527-1/-2)
Flexural modulus
MPa
4500* (ISO 178)
Heat deflection temperature (HDT/A, 1.8 MPa)
°C
100* (ISO 75-2)
Melting temperature (Tm)
°C
220* (ISO 11357-3)
Water absorption (24 h, 23 °C)
%
1.5* (ISO 62)
Mold shrinkage (flow direction)
%
0.5* (ISO 294-4)
Mold shrinkage (transverse direction)
%
0.9* (ISO 294-4)
*
Typical data for this polymer class, for reference.
Указанные показатели измеряются по внутренним методикам, близким к соответствующим ISO, ГОСТ
Информация носит ознакомительный характер, рекомендуем использовать техническую информацию после согласования с поставщиком и подписания нормативно-технической спецификации