Examid\u00ae PA66 CF30 Y is a polyamide 66 reinforced with 30% carbon fiber. Top of the line in specific stiffness: tensile modulus of 22,000 MPa at a density of only 1.30 g\/cm\u00b3. For comparison, PA66 GF50 delivers 16,800 MPa at 1.56 g\/cm\u00b3 \u2014 carbon fiber wins on both stiffness and weight simultaneously.<\/p>\n
Tensile strength of 280 MPa, flexural strength of 290 MPa, HDT of 230 \u00b0C at 1.80 MPa \u2014 a working metal-replacement tool: brackets, levers, drive housings, UAV structures, sports equipment. Carbon fiber adds electrical conductivity and improved friction behavior as a bonus.<\/p>\n
The PA66 matrix provides a 260 \u00b0C melting point and stable service at 120\u2013150 \u00b0C. Processing: melt 280\u2013300 \u00b0C, mold 100\u2013120 \u00b0C. The grade is a cost-efficient alternative to imported PA66 CF30 compounds.<\/p>\n
<\/p>","protected":false},"excerpt":{"rendered":"
Description Examid\u00ae PA66 CF30 Y is a polyamide 66 reinforced with 30% carbon fiber. Top of the line in specific stiffness: tensile modulus of 22,000 MPa at a density of only 1.30 g\/cm\u00b3. For comparison, PA66 GF50 delivers 16,800 MPa at 1.56 g\/cm\u00b3 \u2014 carbon fiber wins on both stiffness and weight simultaneously. Tensile strength […]<\/p>\n","protected":false},"author":1,"featured_media":0,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"footnotes":""},"categories":[19,6],"tags":[],"class_list":["post-5683","post","type-post","status-publish","format-standard","hentry","category-pa-cf","category-polyamides"],"yoast_head":"\n